430 304 304L 316L 201 316 4x8 sheet metal prices stainless steel
Product Description
1. Specifications about stainless steel sheet
| Commodity | 430 304 304L 316L 201 316 4x8 sheet metal prices stainless steel |
| Grade | 201,202,304,304L,316,316L,310S,309S,321,301,310,410,420,430,904L |
| Brand | TISCO ,BAOSTEEL,POSCO,JISCO,LISCO |
| Certification | SGS,BV,IQI,TUV,ISO,etc |
| Thickness | 0.2mm-150mm |
| Width | 1000,1219,1250,1500mm, or as your requirements |
| Length | 2000,2438,2500,3000,6000mm, or as your requirements |
| Surface | No.1, 2B, BA, 8K Mirror, Hairline,satin, Embossed,brush,No.4,HL,matt,pvc film,laser film. |
| Standard | ASTM,AISI,SUS,JIS,EN,DIN,GB, ASME,etc |
| Delivery time | 5-7 days after confirming the order |
| MOQ | 1 Ton |
| Advantages | Showing the splendor of your quality, wearresistant as well , strong corrosion resistance and decorative effect, durable and beautiful in good taste. |
2. Production Flow about stainless steel sheet
Raw materials are sending to hot rolling units for rolling into different sizes
- Hot rolled material is annealing in cold; rolled annealing furnace and pickling in acid.
- All mill rolls are grinded on precision grinding machine with proper chamfering after first shiftoperation.
- All sheets are pickled in different tanks and dried on brush roll machine before dispatched.
- These sheets are again annealing and are sent to straighten machine for straightening.
- Inspections are done at various stages. Keep proper control overall internal process via rolling,annealin and pickling by our experienced staff
Applications
- Oil and gas industry equipment
- Offshore platforms, heat exchangers, process and service water systems, fire-fighting systems, injection and ballast water systems
- Chemical process industries, heat exchangers, vessels, and piping
- Desalination plants, high pressure RO-plant and seawater piping
- Mechanical and structural components, high strength, corrosion-resistant parts
- Power industry FGD systems, utility and industrial scrubber systems, absorber towers, ducting, and piping
Low Temperature Impact Properties
| Temperature °F | RT | 32 | -4 | -40 |
| Ft-lbs | 162 | 162 | 155 | 140 |
| Temperature °F | -76 | -112 | -148 | -320 |
| Ft-lbs | 110 | 44 | 30 | 7 |
Elevated Temperature Tensile Properties
| Temperature °F | 68 | 212 | 302 | 392 | 482 |
| 0.2% Offset Yield Strength, ksi | 80 | 65 | 61 | 58 | 55 |
| Ultimate Tensile Strength, ksi | 116 | 101 | 98 | 95 | 94 |
Values obtained for hot rolled plates (th ≤ 2"). Alloy 2304 must not be used for a long time at temperatures higher than 300°C (572°F), where precipitation hardening phenomenon occurs.
Toughness Values (KCV Minimum Values)
| Temp. | -50°C | +20°C | -60°F | +70°F |
| Single | 75 J/cm_ | 90 J/cm_ | 54 ft. lbs | 65 ft. lbs |
| Average (5) | 90 J/cm_ | 150 J/cm | 65 ft. lbs | 87 ft. lbs |
Hardness (Typical Values)
| Average (5) | HV10 180-230 | HB : 180-230 | HRC _ 20 |
Physical Properties
Density : 7,800 kg/m3 - 0.28 lb/in3
Interval
Temper
°C | Thermal
expansion
ax10M-bK-1 | °C
| Resistivity
(μ_ cm) | Thermal
conductivity
(W.m-1.K-1) | Specific
heat
(J.kg-1.K-1 | Young
modulus
E
(GPa) | Shear
modulus
G
(GPa) |
| 20-100 | 13 | 20 | 80 | 17 | 450 | 200 | 75 |
| 20-100 | 13 | 100 | 92 | 18 | 500 | 190 | 73 |
| 20-200 | 13.5 | 200 | 100 | 19 | 530 | 180 | 70 |
| 20-300 | 14 | 300 | 105 | 20 | 560 | 170 | 67 |