410 stainless steel properties
Type 410 SS is a hardenable, martensitic stainless steel. It combines the superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainless. It features high strength, heat resistance, and good ductility. Good corrosion resistance in mild atmospheres, steam and mild chemical environments make it well suited for highly stressed parts. This grade of 410 stainless steel is magnetic in both the annealed and hardened conditions.
Our 410 stainless steel materials are used in aerospace, automotive, petrochemical and medical applications. Grade 410 SS is also used in manufacturing of products like springs and fasteners, as it can be machined after tempering or annealing. For free machining applications that do not require the higher corrosion resistance of 410, consider our grade of 416 stainless instead.
410 stainless steel Standard Inventory Specifications
UNS S41000 AMS 5504 AMS 5613 (Chemistry only)
ASTM A 240 ASTM A 276 ASTM A 493
ASTM F 899 ASME SA 240 B50991B
410 stainless steel Chemical Composition
| | Element | Percent by Weight |
| C | Carbon | 0.15 max |
| Mn | Manganese | 1.00 max |
| Si | Silicon | 1.00 max |
| Cr | Chromium | 11.50 - 13.50 |
| C | Nickel | 0.75 max |
| S | Sulfur | 0.03 max |
| P | Phosphorus | 0.04 max |
410 Stainles Steel Physical Properties
The values reported below are typical for Type 410 alloy in the annealed condition.
410 stainless steel Coefficient of Thermal Expansion
| Temperature Range | Coefficients |
| °C | °F | cm/cm/°C | in/in/°F |
| 20-200 | 68-392 | 10.5 x10-6 | 5.9 x 10-6 |
| 20-600 | 68-1112 | 11.6 x 10-6 | 6.5 x 10-6 |
410 stainless steel Thermal Conductivity
| Temperature Range | W/m·K | Btu/(hr · ft · °F) |
| °C | °F |
| 100 | 212 | (0.249) | 14.4 |
410 stainless steel Specific Heat
410 stainless steel Electrical Resistivity
| Temperature Range | microhm-cm |
| °C | °F |
| 20 | 68 | 56 |
410 stainless steel Mechanical Properties and Yield Strength
| Typical Annealed Properties | Hardening Response HRC |
| HRB | 0.2% Offset
Yield Strength
Ksi (MPa) | Tensile Strength
Ksi (MPa) | Elongation, Percent in 2" (51 mm) |
| 82-96 | 30 (205) - 42 (290) | 65 (450) - 74 (510) | 20 -34 | 38-45 |
410 stainless steel Common Trade Names
410 stainless steel Common Applications
-
Aerospace structures
-
Automotive exhausts, manifolds and high temperature engine components
-
Medical instruments and devices
-
Petro-chemical applications
-
Cutlery, kitchen utensils
-
Flat springs
-
Hand tools